Titanium Grade 2 is commercially pure titanium and the workhorse of the titanium family. It gives excellent corrosion resistance in seawater, chlorides and oxidising acids thanks to a self-repairing oxide film, combined with good ductility, formability and weldability. Roughly half the weight of steel, it is specified across desalination, chemical processing and marine engineering.
Sarovar Tube Industries manufactures, stocks and exports Titanium Grade 2 Sheets from Mumbai to customers across the Middle East, South East Asia, Europe, Africa and the Americas. Every heat is verified by in-house testing before despatch and supported by complete documentation, so the material you receive is exactly the material you specified.
The table below sets out the standard manufacturing range for Titanium Grade 2 Sheets. Sizes and finishes outside this range are produced against firm orders.
| Parameter | Details |
|---|---|
| Thickness Range | 0.5 mm to 5.0 mm |
| Width | 1000 mm, 1220 mm, 1250 mm, 1500 mm, 2000 mm |
| Length | 2000 mm, 2440 mm, 2500 mm, 3000 mm, coil lengths |
| Form | Cold rolled sheet, coil, strip, shim, blanks, chequered sheet |
| Surface | Mill finish, 2B, BA, No.4 brushed, PVC coated, anodised |
| Edge | Mill edge, slit edge, deburred |
| Dimensional Standard | ASTM A480 / B209 / EN 485 as applicable |
| Value Addition | Shearing, laser cutting, bending and forming to drawing |
| Description | Details |
|---|---|
| Primary Standard | ASTM B348 / B265 / B363 / B381, UNS R50400 |
| Grade Designation | Titanium Grade 2 |
| Equivalent Grades | Ti Gr 2, DIN 3.7035, WL 3.7035, JIS Class 2, Ti-CP2 |
| Product Category | Titanium - Sheets |
| Certification | EN 10204 3.1 as standard, 3.2 with third party inspection on request |
| Thickness (mm) | Standard Width (mm) | Standard Length (mm) | Typical Supply |
|---|---|---|---|
| 0.5 - 0.8 | 1000 / 1250 | 2000 / 2500 | Sheet / coil |
| 1.0 - 1.5 | 1250 / 1500 | 2500 / 3000 | Sheet / coil |
| 1.6 - 2.0 | 1250 / 1500 | 2500 / 3000 | Sheet |
| 2.5 - 3.0 | 1500 / 2000 | 3000 / 6000 | Sheet |
| 3.5 - 4.0 | 1500 / 2000 | 3000 / 6000 | Sheet |
| 4.5 - 5.0 | 1500 / 2000 | 3000 / 6000 | Sheet / light plate |
Thickness and width tolerances per the governing product standard. Slit coil and cut blanks supplied to customer sizes.
Composition limits in weight percent as required by ASTM B348 / B265 / B363 / B381, UNS R50400. Every heat is verified by spectrographic analysis and positive material identification.
| Element | Composition (%) |
|---|---|
| Nitrogen (N) | 0.03 max |
| Carbon (C) | 0.08 max |
| Hydrogen (H) | 0.015 max |
| Iron (Fe) | 0.30 max |
| Oxygen (O) | 0.25 max |
| Titanium (Ti) | Balance |
Minimum room temperature properties in the supplied condition. Results for the actual heat supplied are recorded on the mill test certificate.
| Property | Value |
|---|---|
| Tensile Strength | 345 MPa (50,000 psi) min |
| Yield Strength | 275 - 450 MPa |
| Elongation | 20% min |
| Hardness | approx. 160 HB |
| Modulus of Elasticity | 103 GPa |
| Density | 4.51 g/cm3 |
Material is released only after the following checks are completed and recorded:
Titanium Grade 2 Sheets is specified across the following industries and services:
All material is manufactured and tested to ASTM B348 / B265 / B363 / B381, UNS R50400. Equivalent grades include Ti Gr 2, DIN 3.7035, WL 3.7035, JIS Class 2, Ti-CP2. The governing standard is printed on every mill test certificate.
Every consignment ships with an EN 10204 3.1 mill test certificate covering heat-wise chemical analysis and mechanical properties. Type 3.2 certification with third party inspection by TUV, SGS, BV or Lloyd's is available when specified at the enquiry stage.
Yes. Beyond the standard range shown above we manufacture to customer drawings and specifications, including special lengths, non-standard wall thickness and machined profiles. Share your drawing with the enquiry and our technical team will confirm feasibility and lead time.
Stock items are despatched within three to five working days of order confirmation. Made-to-order material typically takes four to six weeks depending on grade, size and heat treatment requirements. Export documentation and packing are handled in house.
Custom fabrication, special sizes and complete export documentation are handled in house. Send us your drawing or specification and our technical team will come back with a detailed offer, usually within one working day.