Titanium Grade 5, the alpha-beta alloy Ti-6Al-4V, accounts for more than half of all titanium used worldwide. Aluminium and vanadium additions roughly triple the strength of commercially pure titanium while retaining excellent corrosion resistance and a very high strength to weight ratio, making it standard for aerospace structures, medical implants and critical high-load hardware.
Sarovar Tube Industries manufactures, stocks and exports Titanium Grade 5 Round Rods from Mumbai to customers across the Middle East, South East Asia, Europe, Africa and the Americas. Every heat is verified by in-house testing before despatch and supported by complete documentation, so the material you receive is exactly the material you specified.
The table below sets out the standard manufacturing range for Titanium Grade 5 Round Rods. Sizes and finishes outside this range are produced against firm orders.
| Parameter | Details |
|---|---|
| Diameter Range | 4 mm to 500 mm |
| Length | Up to 6000 mm, cut lengths from 100 mm |
| Form | Round bar, rod, billet, forged bar, hollow bar |
| Finish | Hot rolled, cold drawn, peeled and turned, ground, polished, black |
| Tolerance | h9, h11, k12 and custom tolerances on request |
| Condition | Annealed, normalised, solution treated, aged, stress relieved |
| Dimensional Standard | ASTM B221 / B348 / EN 755 as applicable |
| Straightness | Precision straightened for CNC bar feeders |
| Description | Details |
|---|---|
| Primary Standard | ASTM B348 / B265 / B381 / AMS 4911, UNS R56400 |
| Grade Designation | Titanium Grade 5 (Ti-6Al-4V) |
| Equivalent Grades | Ti-6Al-4V, DIN 3.7165, WL 3.7164, AMS 4928, JIS Class 60 |
| Product Category | Titanium - Round Rods |
| Certification | EN 10204 3.1 as standard, 3.2 with third party inspection on request |
| Diameter (mm) | Diameter (inch approx.) | Typical Finish | Standard Length (mm) |
|---|---|---|---|
| 4 - 10 | 5/32 - 3/8 | Cold drawn / ground | 3000 / 4000 |
| 12 - 25 | 1/2 - 1 | Cold drawn / peeled | 3000 / 6000 |
| 28 - 50 | 1 1/8 - 2 | Peeled and turned | 3000 / 6000 |
| 55 - 100 | 2 1/4 - 4 | Peeled / hot rolled | 3000 / 6000 |
| 110 - 200 | 4 1/2 - 8 | Hot rolled / forged | 3000 / 6000 |
| 210 - 350 | 8 1/4 - 14 | Forged and machined | Cut to length |
| 360 - 500 | 14 1/4 - 20 | Forged and machined | Cut to length |
Intermediate diameters and close machining tolerances available. Saw cutting to exact billet length supplied on request.
Composition limits in weight percent as required by ASTM B348 / B265 / B381 / AMS 4911, UNS R56400. Every heat is verified by spectrographic analysis and positive material identification.
| Element | Composition (%) |
|---|---|
| Aluminium (Al) | 5.50 - 6.75 |
| Vanadium (V) | 3.50 - 4.50 |
| Iron (Fe) | 0.40 max |
| Oxygen (O) | 0.20 max |
| Carbon (C) | 0.08 max |
| Nitrogen (N) | 0.05 max |
| Hydrogen (H) | 0.015 max |
| Titanium (Ti) | Balance |
Minimum room temperature properties in the supplied condition. Results for the actual heat supplied are recorded on the mill test certificate.
| Property | Value |
|---|---|
| Tensile Strength | 895 MPa (130,000 psi) min |
| Yield Strength | 828 MPa (120,000 psi) min |
| Elongation | 10% min |
| Hardness | approx. 334 HB (36 HRC) |
| Modulus of Elasticity | 114 GPa |
| Density | 4.43 g/cm3 |
Material is released only after the following checks are completed and recorded:
Titanium Grade 5 Round Rods is specified across the following industries and services:
All material is manufactured and tested to ASTM B348 / B265 / B381 / AMS 4911, UNS R56400. Equivalent grades include Ti-6Al-4V, DIN 3.7165, WL 3.7164, AMS 4928, JIS Class 60. The governing standard is printed on every mill test certificate.
Every consignment ships with an EN 10204 3.1 mill test certificate covering heat-wise chemical analysis and mechanical properties. Type 3.2 certification with third party inspection by TUV, SGS, BV or Lloyd's is available when specified at the enquiry stage.
Yes. Beyond the standard range shown above we manufacture to customer drawings and specifications, including special lengths, non-standard wall thickness and machined profiles. Share your drawing with the enquiry and our technical team will confirm feasibility and lead time.
Stock items are despatched within three to five working days of order confirmation. Made-to-order material typically takes four to six weeks depending on grade, size and heat treatment requirements. Export documentation and packing are handled in house.
Custom fabrication, special sizes and complete export documentation are handled in house. Send us your drawing or specification and our technical team will come back with a detailed offer, usually within one working day.